Jul 04, 2018 Yttria-reinforced copper matrix composites were prepared by dry ball milling (DBM) and wet ball milling (WBM), respectively, followed by spark plasma sintering (SPS). It is to determine which milling process is better for fabricating Cu–Y2O3 composites. It is found that Cu–Y2O3 composites synthesized by DBM exhibit better densification, mechanical and electrical properties than those by.
Oct 01, 2021 AA7075–0.5 wt Y 2 O 3 powders were mechanically alloyed (MA) in a RETSCH-PM 100 planetary mill at a rotation rate of 400 rpm for various milling times (0.25, 1, 1.5, 2, and 10 h). Besides, pure AA7075 (unmilled) was utilized as a reference sample for comparison purposes. The 10 mm diameter tungsten carbide (WC) balls in a tungsten carbide jar were used, and the ball-to-powder.